- LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Low to None Ion Content, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 161 MPa | 23400 psi | ASTM D638 |
| Tensile Strength, Yield | 137 MPa | 19900 psi | ISO 527-1, -2 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.18 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.48 J/cm @Thickness 3.18 mm |
8.39 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 5.10 kJ/m² | 2.43 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 28.2 kJ/m² | 13.4 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 11.4 J | 8.41 ft-lb | ASTM D3763 |
| Impact Test | 2.41 J | 1.78 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.0 µm/m-°C @Temperature 20.0 °C |
17.8 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature 20.0 °C |
17.8 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D4496 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 360 - 366 °C | 680 - 691 °F | |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi |