LNP Stat-Kon® OC-1006 Polyphenylene Sulfide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® OC-1006 Polyphenylene Sulfide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
ASTM D638
Tensile Strength, Yield 210 MPa
30500 psi
ASTM D638
Elongation at Break 1.1 %
1.1 %
ASTM D638
Elongation at Yield 1.1 %
1.1 %
ASTM D638
Tensile Modulus 32.8 GPa
4760 ksi
ASTM D638
Flexural Strength 303 MPa
43900 psi
ASTM D790
Flexural Modulus 23.5 GPa
3410 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm

@Thickness 3.18 mm
0.899 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.38 J/cm

@Thickness 3.18 mm
8.21 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 5.20 kJ/m²
2.47 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 28.1 kJ/m²
13.4 ft-lb/in²
ISO 180
Falling Dart Impact 3.30 J
2.43 ft-lb
ASTM D3763
Impact Test 1.70 J
1.25 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 1.6
1.6
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 1.4
1.4
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 1730 x 10-8 mm³/N-M
857 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 267 °C
513 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D4496
Processing Properties Metric English Comments
Melt Temperature 316 - 321 °C
601 - 610 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi