LNP Stat-Kon® LCL-4026 EM BK8-115 Polyetheretherketone, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant  (d

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® LCL-4026 EM BK8-115 Polyetheretherketone, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant  (d.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically Conductive, Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
ASTM D638
Flexural Modulus 20.1 GPa
2920 ksi
ASTM D790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.18 mm
0.800 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.27 J/cm

@Thickness 3.18 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Processing Properties Metric English Comments
Melt Temperature 379 - 388 °C
714 - 730 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.010 %
0.010 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Color Black