Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

LNP Stat-Kon® EC-1008 EM BK8-115 Polyetherimide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Stat-Kon® EC-1008 EM BK8-115 Polyetherimide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically Conductive, Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.00 cm/cm
0.00 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 222 MPa
32200 psi
ASTM D638
Elongation at Break 1.5 %
1.5 %
ASTM D638
Flexural Strength 310 MPa
45000 psi
ASTM D790
Flexural Modulus 25.5 GPa
3700 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.18 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.27 J/cm

@Thickness 3.18 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Coefficient of Friction, Dynamic 0.50
0.50
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.46
0.46
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 141 x 10-8 mm³/N-M
70.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Processing Properties Metric English Comments
Melt Temperature 360 - 366 °C
680 - 691 °F
Mold Temperature 121 - 149 °C
250 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Color Black
Users viewing this material also viewed the following: