LNP Lubricomp® PDX-U-95672 BK8-115 Polyphthalamide, Proprietary Filler  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® PDX-U-95672 BK8-115 Polyphthalamide, Proprietary Filler  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
Method A; ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength at Break 163 MPa
23600 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Tensile Modulus 12.8 GPa
1860 ksi
ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 11.2 GPa
1620 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.18 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 6.30 J/cm

@Thickness 3.18 mm
11.8 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.30 kJ/m²
3.00 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 44.0 kJ/m²
20.9 ft-lb/in²
ISO 180
Falling Dart Impact 4.10 J
3.02 ft-lb
ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 321 - 349 °C
610 - 660 °F
Mold Temperature 48.9 - 104 °C
120 - 219 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Color Black