LNP Lubricomp® PDX-E-00548 CCS Polyetherimide, Aramid Fiber Reinforced, PTFE Lubricant  (discontinued **)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Aramid Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® PDX-E-00548 CCS Polyetherimide, Aramid Fiber Reinforced, PTFE Lubricant  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Lubricated, Low to None Ion ContentForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
Method A; ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.4 MPa
12100 psi
ASTM D638
Tensile Strength, Yield 84.8 MPa
12300 psi
ASTM D638
Elongation at Break 8.1 %
8.1 %
ASTM D638
Elongation at Yield 6.1 %
6.1 %
ASTM D638
Tensile Modulus 3.03 GPa
439 ksi
ASTM D638
Flexural Strength 145 MPa
21000 psi
ASTM D790
Flexural Modulus 3.45 GPa
500 ksi
ASTM D790
Izod Impact, Notched 0.267 J/cm

@Thickness 3.18 mm
0.500 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.70 J/cm

@Thickness 3.18 mm
8.81 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 4.70 kJ/m²
2.24 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 32.6 kJ/m²
15.5 ft-lb/in²
ISO 180
Falling Dart Impact 4.90 J
3.61 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 360 - 366 °C
680 - 691 °F
Mold Temperature 121 - 149 °C
250 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi