LNP Lubricomp® OFL-4036 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® OFL-4036 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.69 g/cc
1.69 g/cc
Method A; ASTM D792
Density 1.69 g/cc
0.0611 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ASTM D638
Tensile Strength, Yield 145 MPa
21000 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Elongation at Yield 1.7 %
1.7 %
ASTM D638
Tensile Modulus 12.3 GPa
1780 ksi
ASTM D638
Flexural Strength 200 MPa
29000 psi
ASTM D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D790
Izod Impact, Notched 0.854 J/cm

@Thickness 3.18 mm
1.60 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 5.50 J/cm

@Thickness 3.18 mm
10.3 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 9.40 kJ/m²
4.47 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 26.4 kJ/m²
12.6 ft-lb/in²
ISO 180
Falling Dart Impact 3.40 J
2.51 ft-lb
ASTM D3763
Impact Test 1.97 J
1.45 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.44
0.44
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.35
0.35
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 66.5 x 10-8 mm³/N-M
33.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 269 °C
516 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 - 321 °C
601 - 610 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi