LNP Lubricomp® FL-4410 Polyetherimide, Silicone Lubricant Additive (discontinued **)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Lubricomp® FL-4410 Polyetherimide, Silicone Lubricant Additive (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	0.950 g/cc	0.950 g/cc	Method A; ASTM D792
Density	0.950 g/cc	0.0343 lb/in³	ISO 1183
Linear Mold Shrinkage	0.021 - 0.023 cm/cm	0.021 - 0.023 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.016 - 0.017 cm/cm	0.016 - 0.017 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	26.9 MPa	3900 psi	ASTM D638
Elongation at Yield	0.70 %	0.70 %	ASTM D638
Tensile Modulus	0.758 GPa	110 ksi	ASTM D638
Flexural Strength	20.7 MPa	3000 psi	ASTM D790
Flexural Modulus	0.896 GPa	130 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm @Thickness 3.18 mm	3.00 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	NB @Thickness 3.18 mm	NB @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	10.0 kJ/m²	4.76 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	120 kJ/m²	57.1 ft-lb/in²	ISO 180
Falling Dart Impact	21.4 J	15.8 ft-lb	ASTM D3763
Impact Test	28.7 J	21.2 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic	0.11	0.11	vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static	0.11	0.11	vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor	56.4 x 10^-8 mm³/N-M	28.0 x 10^-10 in³-min/ft-lb-hr	40psi, 50ft/min; tested in accordance with LNP WI-0687

Thermal Properties	Metric	English	Comments
CTE, linear	120 µm/m-°C @Temperature 20.0 °C	66.7 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	130 µm/m-°C @Temperature 20.0 °C	72.2 µin/in-°F @Temperature 68.0 °F	TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi)	47.2 °C	117 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	232 °C	450 °F
Mold Temperature	37.8 - 51.7 °C	100 - 125 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4 hour	4 hour
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi

Users viewing this material also viewed the following: