LG Chemical TR557 MABS, High Transparency, High Impact

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical TR557 MABS, High Transparency, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, High Transparency, High ImpactApplication: Electric/Electronic Applications, Copier, Printer etc.CAS No. 9011-14–7 and 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Melt Flow 23 g/10 min

@Load 10.0 kg,
Temperature 220 °C
23 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D785
Tensile Strength, Yield 45.1 MPa

@Thickness 3.20 mm
6540 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
30 %

@Thickness 0.126 in
50 mm/min; ASTM D638
Flexural Yield Strength 72.6 MPa

@Thickness 6.40 mm
10500 psi

@Thickness 0.252 in
15 mm/min; ASTM D790
Flexural Modulus 2.22 GPa

@Thickness 6.40 mm
321 ksi

@Thickness 0.252 in
15 mm/min; ASTM D790
Izod Impact, Notched 1.57 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.94 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
1.67 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
3.12 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C

@Thickness 6.40 mm
178 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
122 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
HB

@Thickness >=0.118 in
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ASTM D1003
Transmission, Visible 90 %
90 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Strength 7.00 kV/mm
178 kV/in
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
7.0 - 15 sec

@Thickness >=0.0591 in
7.0 - 15 sec

@Thickness >=3.00 mm
7.0 - 15 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
Users viewing this material also viewed the following: