LG Chemical TR-557I Transparent ABS, High Impact, Ice Colored Pellets
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical TR-557I Transparent ABS, High Impact, Ice Colored Pellets.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electronic parts, OA machines, toys and others that require transparency and high impact strength. An Izod impact strength or falling dart impact strength of LG transparent ABS is relatively similar to that of general ABS, it is not easily cracked like SAN or PMMA resin in the condition of low impact energy. TR-557 series is good for applications requiring high impact strength.Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Index of Compound | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 41.19 MPa | 5974 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 63.74 MPa | 9245 psi | ASTM D790 |
| Flexural Modulus | 1.99 GPa | 289 ksi | ASTM D790 |
| Izod Impact, Notched | 1.471 J/cm | 2.756 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | |
| Transmission, Visible | 89.5 % | 89.5 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 200 °C | 374 - 392 °F | Extrusion cylinder temperature, C1 |
| 210 - 225 °C | 410 - 437 °F | Extrusion cylinder temperature, C2 | |
| 230 - 240 °C | 446 - 464 °F | Extrusion cylinder temperature, C3 | |
| 240 - 250 °C | 464 - 482 °F | Extrusion cylinder temperature, C4 and C5 | |
| Rear Barrel Temperature | 190 - 200 °C | 374 - 392 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | |
| Adapter Temperature | 235 - 245 °C | 455 - 473 °F | |
| Die Temperature | 113 - 118 °C | 235 - 245 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Injection molding |
| 255 - 260 °C | 491 - 500 °F | Extrusion | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Roll Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Bottom |
| 80.0 - 90.0 °C | 176 - 194 °F | Middle | |
| 85.0 - 95.0 °C | 185 - 203 °F | Top | |
| Injection Pressure | 68.65 - 88.26 MPa | 9957 - 12800 psi | Second |
| 58.84 - 98.1 MPa | 8534 - 14200 psi | First | |
| Back Pressure | 0.490 - 1.96 MPa | 71.1 - 284 psi | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- Polymer Resources NY66-IM1-G13-[color]-H Nylon 66, 13% Glass Reinforced, Toughened and Heat Stabilized
- Huntsman AroCy XU 71787.02 L Cyanate Ester
- Flint Hills P9G8Z-036 Polypropylene Specialty Polypropylene
- Techmer ES HiFill® ABS GM30 LE 30% Glass Filled
- SABIC Innovative Plastics NORYL PX2949 PPE+PS (Asia Pacific)
- ExxonMobil SAE 40 Mobilgard ADL Series
- NAPCO C85 - RK Bauxite
- Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content
- CLAL-MSX NICLAFOR® 1000 TH4 Quenched/Precipitation Heat Treated, Drawn Copper Alloy
- Fainplast Compounds MPH 67 Medical Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved