| Category | Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC ES440 Ethylene Vinyl Acetate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Good Mechanical Properties and Good Optical PropertiesApplications: Agricultural Film, Shoe solesCSA No. 24937-78-8Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.933 - 0.938 g/cc | 0.933 - 0.938 g/cc | ASTM D1505 |
| Melt Flow | 0.30 - 1.7 g/10 min @Load 2.61 kg, Temperature 190 °C |
0.30 - 1.7 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 21.6 MPa | 3130 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 400 % | 400 % | 500 mm/min; ASTM D638 |
| Film Elongation at Break, TD | 700 % | 700 % | 500 mm/min; ASTM D638 |
| Elongation at Break | 700 % | 700 % | 500 mm/min; ASTM D638 |
| 2% Secant Modulus | 0.350 GPa | 50.8 ksi | 500mm/min; ASTM D638 |
| Dart Drop Test | >= 400 g | >= 0.882 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 31.4 MPa | 4550 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 31.4 MPa | 4550 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 87.0 °C | 189 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 66.0 °C | 151 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.8 % | 1.8 % | ASTM D1003 |
| Gloss | 120 % | 120 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- MV Labs YB300 Yb2(CO3)3·xH2O Ytterbium carbonate hydrate
- Pinnacle Polymers 1220 Polypropylene Homopolymer, Injection Molding Grade
- Kazanorgsintez Polyethyleneglycol, Dust Controller
- Industeel CLC 18.10 LN Nitrogen Containing 18Cr-10Ni Austenitic Stainless Steel
- Momentive Performance Materials Addisilâ„¢ 470 E Healthcare Extrusion Grade Heat Cured Rubber
- Zeon Chemicals Quintone® D200 Aliphatic Hydrocarbon Resin
- Dow Corning SILASTIC® 3497 MOULD MAKING BASE & 96 CURING AGENT
- Bapolene® 4042 Polypropylene, Fiber/Filament Grade
- LATI Latimass 82-03 D110 PA12
Copyright © lookpolymers.com All Rights Reserved