LG Chemical Lupox® HI2100M PBT+GF10%

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name Lupox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® HI2100M PBT+GF10%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+GF10%, High ImpactApplication: IT/OA, E&E (Bobbin, Switch)CAS No. 65997-17-3, 155123-66-3 and 30965-26-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0070 - 0.011 cm/cm

@Thickness 3.20 mm
0.0070 - 0.011 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 74.5 MPa

@Thickness 3.20 mm
10800 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 5.0 %

@Thickness 3.20 mm
5.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 3.82 GPa

@Thickness 3.20 mm
555 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 0.422 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
0.790 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 185 °C

@Thickness 6.40 mm
365 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding