LG Chemical Lupox® GP2200 PBT+GF20%

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name Lupox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® GP2200 PBT+GF20%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+GF20%, General Purpose Application: IT/OA, E&E, Automotive (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.011 cm/cm

@Thickness 3.20 mm
0.0040 - 0.011 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 108 MPa

@Thickness 3.20 mm
15700 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 4.0 %

@Thickness 3.20 mm
4.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 157 MPa

@Thickness 3.20 mm
22800 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 6.28 GPa

@Thickness 3.20 mm
910 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.10 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 200 °C

@Thickness 6.40 mm
392 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 140 °C

@Thickness >=0.710 mm
284 °F

@Thickness >=0.0280 in
140 °C

@Thickness >=1.50 mm
284 °F

@Thickness >=0.0591 in
140 °C

@Thickness >=3.00 mm
284 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 120 °C

@Thickness >=0.710 mm
248 °F

@Thickness >=0.0280 in
120 °C

@Thickness >=1.50 mm
248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
248 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 140 °C

@Thickness >=0.710 mm
284 °F

@Thickness >=0.0280 in
140 °C

@Thickness >=1.50 mm
284 °F

@Thickness >=0.0591 in
140 °C

@Thickness >=3.00 mm
284 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=0.710 mm
HB

@Thickness >=0.0280 in
HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 23.0 kV/mm

@Thickness 1.00 mm
584 kV/in

@Thickness 0.0394 in
ASTM D149
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding