LG Chemical LUPOY SG5009F PC/ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY SG5009F PC/ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, High Gloss, Scratch Resistance, Halogen Free Flame RetardantApplication: IT&OA (Notebook PC & Monitor housing)CAS: 103598-77-2 and 181028-79-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.040
0.040
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 250 °C
15 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.7 MPa

@Thickness 3.20 mm
9670 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 103 MPa

@Thickness 3.20 mm
14900 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 2.79 GPa

@Thickness 3.20 mm
405 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
0.918 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 6.40 mm
194 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness 1.60 - 1.70 mm
140 °F

@Thickness 0.0630 - 0.0669 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.60 - 1.70 mm
140 °F

@Thickness 0.0630 - 0.0669 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.60 - 1.70 mm
140 °F

@Thickness 0.0630 - 0.0669 in
Flammability, UL94 V-0

@Thickness 1.60 - 1.70 mm
V-0

@Thickness 0.0630 - 0.0669 in
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 270 °C
446 - 518 °F
Injection Molding
Middle Barrel Temperature 235 - 275 °C
455 - 527 °F
Injection Molding
Front Barrel Temperature 235 - 275 °C
455 - 527 °F
Injection Molding
Nozzle Temperature 235 - 275 °C
455 - 527 °F
Injection Molding
Melt Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 1.96 MPa
142 - 284 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding