LG Chemical LUPOY NS5000C PC/ABS, High Impact

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY NS5000C PC/ABS, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High ImpactApplication: Automotive (Interior)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 4.8 g/10 min

@Load 2.16 kg,
Temperature 250 °C
4.8 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength, Yield 53.0 MPa

@Thickness 3.20 mm
7680 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break >= 100 %

@Thickness 3.20 mm
>= 100 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 85.3 MPa

@Thickness 3.20 mm
12400 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 2.16 GPa

@Thickness 3.20 mm
313 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched >= 5.39 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
>= 10.1 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
ASTM D256
>= 6.86 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
>= 12.9 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 114 °C

@Thickness 6.40 mm
237 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Middle Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Front Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Nozzle Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection Molding
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding