LG Chemical LUPOL TE-5104K Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Modulus

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	LG Chemical
Trade Name	LUPOL
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LG Chemical LUPOL TE-5104K Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Modulus.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive exterior parts.Information Provided by LG Chem

Physical Properties	Metric	English	Comments
Specific Gravity	0.950 g/cc	0.950 g/cc	ASTM D792
Linear Mold Shrinkage	0.0080 cm/cm	0.0080 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	20.0 MPa	2900 psi	ASTM D638
Elongation at Break	>= 300 %	>= 300 %	ASTM D638
Flexural Strength	24.0 MPa	3480 psi	ASTM D790
Flexural Modulus	1.18 GPa	171 ksi	ASTM D790
Izod Impact, Notched	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	115 Â°C	239 Â°F	ASTM D648

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	200 - 220 Â°C	392 - 428 Â°F
Middle Barrel Temperature	200 - 230 Â°C	392 - 446 Â°F
Front Barrel Temperature	210 - 230 Â°C	410 - 446 Â°F
Nozzle Temperature	210 - 240 Â°C	410 - 464 Â°F
Melt Temperature	210 - 240 Â°C	410 - 464 Â°F
Mold Temperature	40.0 - 90.0 Â°C	104 - 194 Â°F
Drying Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Dry Time	2 - 3 hour	2 - 3 hour
Injection Pressure	29.4 - 118 MPa	4260 - 17100 psi	First
	78.45 - 98.07 MPa	11380 - 14220 psi	Second
Back Pressure	0.490 - 3.92 MPa	71.1 - 569 psi
Screw Speed	40 - 60 rpm	40 - 60 rpm