LG Chemical LUPOL GP3302 PP+MF30%

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer LG Chemical
Trade Name LUPOL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOL GP3302 PP+MF30%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PP+MF30%, General Purpose, Good WeatherabilityApplication: Electrical, Electronic and Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm

@Thickness 3.20 mm
0.0070 - 0.010 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 29.4 MPa

@Thickness 3.20 mm
4270 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
30 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 40.2 MPa

@Thickness 6.40 mm
5830 psi

@Thickness 0.252 in
30mm/min; ASTM D790
Flexural Modulus 3.14 GPa

@Thickness 6.40 mm
455 ksi

@Thickness 0.252 in
30mm/min; ASTM D790
Izod Impact, Notched >= 0.441 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
>= 0.827 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness >=1.50 mm
149 °F

@Thickness >=0.0591 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=1.50 mm
149 °F

@Thickness >=0.0591 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness >=1.50 mm
149 °F

@Thickness >=0.0591 in
Flammability, UL94 HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Middle Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Front Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding