LG Chemical LUMID HM2604AW PA6+GF60%

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID HM2604AW PA6+GF60%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6+GF60%Application: Bath liftInformation provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.69 g/cc
1.69 g/cc
ASTM D792
Water Absorption 0.70 %
0.70 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0050 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 130
130
ASTM D785
Tensile Strength, Yield 206 MPa

@Thickness 3.20 mm
29900 psi

@Thickness 0.126 in
5mm/min; ASTM D638
Elongation at Break 2.0 %

@Thickness 3.20 mm
2.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 304 MPa

@Thickness 3.20 mm
44100 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 15.7 GPa

@Thickness 3.20 mm
2280 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 1.57 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.94 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.0 µm/m-°C
20.0 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 205 °C

@Thickness 6.40 mm
401 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm

@Thickness 1.00 mm
533 kV/in

@Thickness 0.0394 in
ASTM D149
Arc Resistance 180 sec
180 sec
ASTM D495
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 270 °C
482 - 518 °F
Injection Molding
Middle Barrel Temperature 260 - 285 °C
500 - 545 °F
Injection Molding
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Melt Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding