LG Chemical LUMID HI5003A PA6/PO, High Impact, High Flow, Good Paintablility
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI5003A PA6/PO, High Impact, High Flow, Good Paintablility.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6/PO, High Impact, High Flow, Good PaintablilityApplication: Automotive Exterior PartsCAS No. 25038-54-4, 9010-79-1, 9003-07-0 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Temperature 23.0 °C, Time 86400 sec |
0.50 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.015 cm/cm @Thickness 3.20 mm |
0.014 - 0.015 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa @Thickness 3.20 mm |
7400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 50 % @Thickness 3.20 mm |
50 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 70.6 MPa @Thickness 6.40 mm |
10200 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa @Thickness 6.40 mm |
299 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
2.20 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 4.51 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
8.45 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C @Thickness 6.40 mm |
324 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Nozzle Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 70 rpm | 30 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512 (842) (UF) Synthetic Oil
- Nylene® 607 Nylon 6, Extrusion Grade
- S&E Specialty Polymers TufPrene™ 2000-40 SEBS
- Formosa Plastics Formolene® L63565U Rotational Molding LLDPE (discontinued **)
- Zotefoams Plastazote® LD24FM Low Density Polyethylene Foam, Flame Retarded
- A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled)
- Eagle Brass 316L Austenitic Stainless Steel, Annealed
- ChevronTexaco Delo® 400 SAE 30
- API Megol AM DP2217/90PBT SEBS Adhesion Modified Overmolding for Polyesters
Copyright © lookpolymers.com All Rights Reserved