LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6+GF33%, General PurposeApplication: Automotive (Air Intake Manifold, Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Water Absorption 0.70 %
0.70 %
ASTM D570
Maximum Moisture Content 0.090
0.090
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0090 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength, Yield 191 MPa

@Thickness 3.20 mm
27700 psi

@Thickness 0.126 in
5mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
3.0 %

@Thickness 0.126 in
5mm/min; ASTM D638
Flexural Yield Strength 279 MPa

@Thickness 3.20 mm
40500 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Flexural Modulus 9.32 GPa

@Thickness 3.20 mm
1350 ksi

@Thickness 0.126 in
1.3mm/min; ASTM D790
Izod Impact, Notched 1.27 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.39 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ASTM D696
Melting Point 260 °C
500 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 260 °C

@Thickness 6.40 mm
500 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C

@Thickness 6.40 mm
482 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 120 °C

@Thickness >=0.750 mm
248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
248 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness >=0.750 mm
230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.50 mm
230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=3.00 mm
230 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 120 °C

@Thickness >=0.750 mm
248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
248 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=0.750 mm
HB

@Thickness >=0.0295 in
HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 25.0 kV/mm

@Thickness 1.00 mm
635 kV/in

@Thickness 0.0394 in
ASTM D149
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=0.750 mm
15 - 30 sec

@Thickness >=0.0295 in
15 - 30 sec

@Thickness >=1.50 mm
15 - 30 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
>= 120 arcs

@Thickness 0.0295 in
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Middle Barrel Temperature 270 - 285 °C
518 - 545 °F
Injection Molding
Front Barrel Temperature 270 - 290 °C
518 - 554 °F
Injection Molding
Nozzle Temperature 270 - 295 °C
518 - 563 °F
Injection Molding
Melt Temperature 270 - 295 °C
518 - 563 °F
Injection Molding
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding