LG Chemical LUCON PX-9002 Thermally Conductive Thermoplastic

Category Polymer , Thermoplastic
Manufacturer LG Chemical
Trade Name LUCON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON PX-9002 Thermally Conductive Thermoplastic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solving problems associated with build-up of electrostatic charges, electrostatic discharge, and electromagnetic interference. These materials span the surface resistivity spectrum from antistatic through conductive to EMI shielding (100-1012O).Applications: Heat exchanger tube, connector, housing, motor, heat sink, cooling interface padInformation Provided by LG Chem
Physical Properties Metric English Comments
Specific Gravity 1.61 g/cc
1.61 g/cc
ASTM D792
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 81
81
ASTM D785
Tensile Strength at Break 24.0 MPa
3480 psi
ASTM D638
Elongation at Break 58 %
58 %
ASTM D638
Flexural Strength 36.0 MPa
5220 psi
ASTM D790
Flexural Modulus 0.980 GPa
142 ksi
ASTM D790
Izod Impact, Notched 2.06 J/cm
3.86 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity >= 1.00 W/m-K
>= 6.94 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 250 °C
428 - 482 °F
Middle Barrel Temperature 230 - 260 °C
446 - 500 °F
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Drying Temperature 120 - 140 °C
248 - 284 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 39.23 - 78.45 MPa
5690 - 11380 psi
Second
68.7 - 118 MPa
9960 - 17100 psi
First
Back Pressure 0.000 - 3.92 MPa
0.000 - 569 psi
Screw Speed 40 - 80 rpm
40 - 80 rpm