LG Chemical HI100X ABS, High Impact, Semi-Transparency, Flexible
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical HI100X ABS, High Impact, Semi-Transparency, Flexible.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, High Impact, Semi-Transparency, FlexibleApplication: Artificial Nails, Miscellaneous Goods)CAS No. 9010-94-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 17 g/10 min @Load 10.0 kg, Temperature 220 °C |
17 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ASTM D785 |
| Tensile Strength, Yield | 30.4 MPa @Thickness 3.20 mm |
4410 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 40 % @Thickness 3.20 mm |
40 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 47.1 MPa @Thickness 3.20 mm |
6830 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 1.37 GPa @Thickness 3.20 mm |
199 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.04 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
5.69 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 6.40 mm |
167 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
- Pau Tai Unistab BT-11 Organotin Stabilizer Butyl/Octyl Carboxylate Tin
- Mitsubishi Xantar® SF 2230 Polycarbonate-30% Glass Reinforced
- Heatbath/Park Aus-Quench Quenching and Tempering Salt
- SABIC Innovative Plastics LNP LUBRILOY DF202P PC
- Chengdu Polyster 5500 General Grade TPV
- ExxonMobil Escorene® LD 755.CM Molding, extrusion and compounding resin
- Chosun Refractories A64 Special High-Density Gunning Castable
- DuPont Teijin Films Mylar® OL2 Polyester Film, 75 Gauge
- Aremco Pyro-Putty™ 653 High Temperature Ceramic-Metallic Putty, Stainless Filled
Copyright © lookpolymers.com All Rights Reserved