LG Chemical 95HC SAN Resin
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical 95HC SAN Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include make-up cases and other products requiring chemical resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 32 g/10 min @Load 10.0 kg, Temperature 220 °C |
32 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 124 | 124 | ASTM D785 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 3.31 GPa | 480 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 132 MPa | 19100 psi | 50 mm/min; ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | 15 mm/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.35 mm |
198 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 107 °C | 225 °F | 1000 g; ASTM D1525 |
| Flammability, UL94 | HB | HB | 1/8 in |
| HB | HB | 1/16 in | |
| Flame Spread | 25.0 mm/min @Thickness 3.17 mm |
0.984 in/min @Thickness 0.125 in |
FH3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | UL Rating PLC 5 (120-180 sec) |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL Rating PLC 1 (400-600 volts) |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | <= 10.0 mm/min | <= 0.394 in/min | UL Rating PLC 0 (0-10 mm/min) |