LATI Latistat 48/9900-03 EVA

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate; Molded/Extruded
Manufacturer LATI
Trade Name Latistat
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latistat 48/9900-03 EVA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dissipative product based on Ethyl-Vinyl-Acetate (EVA). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Linear Mold Shrinkage, Flow 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
Linear Mold Shrinkage, Transverse 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 10.0 MPa
1450 psi
Elongation at Break >= 100 %
>= 100 %
Elongation at Yield 8.0 %
8.0 %
Tensile Modulus 0.700 GPa
102 ksi
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched NB
NB
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 45.0 °C
113 °F
Deflection Temperature at 1.8 MPa (264 psi) 35.0 °C
95.0 °F
Vicat Softening Point 50.0 °C

@Load 5.00 kg
122 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 400 ohm-cm
400 ohm-cm
Surface Resistance 200 ohm
200 ohm
Processing Properties Metric English Comments
Melt Temperature 210 - 230 °C
410 - 446 °F
Mold Temperature 10.0 - 30.0 °C
50.0 - 86.0 °F
Drying Temperature 70.0 - 80.0 °C

@Time 10800 sec
158 - 176 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa