LATI Latishield 36/AR-08A G/17-V0E ABS, Steel/Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer LATI
Trade Name Latishield
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latishield 36/AR-08A G/17-V0E ABS, Steel/Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMI shielding product based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Steel fibers. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0065 cm/cm
0.0050 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Elongation at Break 1.5 %
1.5 %
Tensile Modulus 5.30 GPa
769 ksi
Charpy Impact Unnotched 0.800 J/cm²
3.81 ft-lb/in²
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 85.0 °C

@Load 5.00 kg
185 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Surface Resistance 50 ohm
50 ohm
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Descriptive Properties Value Comments
Electromagnetic reflection 82 dB
ISO Shrinkage - Pressure 60 MPa