LATI Latiohm 83-07 PD11 CNT PA12, Impact Modified

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 83-07 PD11 CNT PA12, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyamide 12 (PA12), impact modified. Carbon nanotubes. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.10 g/cc	0.0397 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0080 - 0.012 cm/cm	0.0080 - 0.012 in/in
Linear Mold Shrinkage, Transverse	0.0080 - 0.012 cm/cm	0.0080 - 0.012 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	85 %	85 %
Elongation at Yield	20 %	20 %
Tensile Modulus	1.10 GPa	160 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	7.50 J/cmÂ²	35.7 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	100 Â°C	212 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	40.0 Â°C	104 Â°F
Vicat Softening Point	120 Â°C @Load 5.00 kg	248 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	7.00e+7 ohm-cm	7.00e+7 ohm-cm
Surface Resistance	1.00e+7 ohm	1.00e+7 ohm

Processing Properties	Metric	English
Melt Temperature	210 - 240 Â°C	410 - 464 Â°F
Mold Temperature	40.0 - 50.0 Â°C	104 - 122 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: