LATI Latiohm 66-10 H2 CNT CE/10 PA66, 10% Mineral Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Mineral Filled
Manufacturer LATI
Trade Name Latiohm
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 66-10 H2 CNT CE/10 PA66, 10% Mineral Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semiconductive/dissipative product based on Polyamide 66 (PA66). Heat stabilized. Carbon nanotubes. Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.238 g/cc
0.04473 lb/in³
Linear Mold Shrinkage, Flow 0.013 - 0.0165 cm/cm
0.013 - 0.0165 in/in
Linear Mold Shrinkage, Transverse 0.013 - 0.0165 cm/cm
0.013 - 0.0165 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
Elongation at Break 2.7 %
2.7 %
Tensile Modulus 5.00 GPa
725 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.130 J/cm²
0.619 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
473 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+8 ohm-cm
1.00e+8 ohm-cm
Surface Resistance 1.00e+8 ohm
1.00e+8 ohm
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa