LATI Latiohm 57-05 PD01 G/15 PPA, 15% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 57-05 PD01 G/15 PPA, 15% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Semi-aromatic polyamide (PPA). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.34 g/cc	0.0484 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0035 - 0.0065 cm/cm	0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse	0.0075 - 0.0105 cm/cm	0.0075 - 0.0105 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	190 MPa	27600 psi
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	13.6 GPa	1970 ksi
Charpy Impact Unnotched	3.50 J/cmÂ²	16.7 ft-lb/inÂ²
Charpy Impact, Notched	0.350 J/cmÂ²	1.67 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	270 Â°C	518 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	260 Â°C	500 Â°F
Vicat Softening Point	230 Â°C @Load 5.00 kg	446 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	10000 ohm-cm	10000 ohm-cm
Surface Resistance	10000 ohm	10000 ohm

Processing Properties	Metric	English
Melt Temperature	320 - 340 Â°C	608 - 644 Â°F
Mold Temperature	130 - 160 Â°C	266 - 320 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa