LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer LATI
Trade Name Latimass
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 0.780 g/cc
0.0282 lb/in³
Linear Mold Shrinkage, Flow 0.0125 - 0.0155 cm/cm
0.0125 - 0.0155 in/in
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 5.00 MPa
725 psi
Elongation at Break 20 %
20 %
Elongation at Yield 1.5 %
1.5 %
Tensile Modulus 1.05 GPa
152 ksi
Charpy Impact Unnotched 0.600 J/cm²
2.86 ft-lb/in²
Charpy Impact, Notched 0.130 J/cm²
0.619 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 55.0 °C
131 °F
Deflection Temperature at 1.8 MPa (264 psi) 40.0 °C
104 °F
Vicat Softening Point 50.0 °C

@Load 5.00 kg
122 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 220 - 240 °C
428 - 464 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa