LATI Latilub 85-10T G/30 PES, 30% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 85-10T G/30 PES, 30% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyether Sulfone (PES). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0050 cm/cm
0.0035 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0080 cm/cm
0.0065 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
Elongation at Break 1.8 %
1.8 %
Tensile Modulus 8.60 GPa
1250 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Coefficient of Friction, Dynamic 0.20
0.20
Coefficient of Friction, Static 0.28
0.28
K (wear) Factor 18.0 x 10-8 mm³/N-M
8.94 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
428 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 350 - 390 °C
662 - 734 °F
Mold Temperature 150 - 190 °C
302 - 374 °F
Drying Temperature 150 - 180 °C

@Time 10800 sec
302 - 356 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa