LATI Latilub 82-05GR G/30 PA12, 30% Glass Fiber Reinforced, Graphite Filled

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 82-05GR G/30 PA12, 30% Glass Fiber Reinforced, Graphite Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 12 (PA12). Graphite. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 7.80 GPa
1130 ksi
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
Coefficient of Friction, Dynamic 0.28
0.28
Coefficient of Friction, Static 0.32
0.32
K (wear) Factor 15.0 x 10-8 mm³/N-M
7.45 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 170 °C

@Load 5.00 kg
338 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 210 - 230 °C
410 - 446 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa