LATI Latilub 73/13 Y/20 POM, 20% Aramid Fiber Reinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Aramid Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 73/13 Y/20 POM, 20% Aramid Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyoxymethylene (POM). Aramid fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0165 - 0.0195 cm/cm
0.0165 - 0.0195 in/in
Linear Mold Shrinkage, Transverse 0.0175 - 0.021 cm/cm
0.0175 - 0.021 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
Elongation at Break 7.5 %
7.5 %
Elongation at Yield 5.5 %
5.5 %
Tensile Modulus 2.90 GPa
421 ksi
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
Coefficient of Friction, Dynamic 0.14
0.14
Coefficient of Friction, Static 0.18
0.18
K (wear) Factor 4.50 x 10-8 mm³/N-M
2.23 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
284 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 175 - 200 °C
347 - 392 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa