POLYMER SEARCH

LATI Latilub 73/13-10ST POM, Silicone/PTFE Filled

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 73/13-10ST POM, Silicone/PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyoxymethylene (POM). Silicone / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.43 g/cc	0.0517 lb/inÂ³
Linear Mold Shrinkage, Flow	0.021 - 0.024 cm/cm	0.021 - 0.024 in/in
Linear Mold Shrinkage, Transverse	0.0215 - 0.0235 cm/cm	0.0215 - 0.0235 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	50.0 MPa	7250 psi
Elongation at Break	40 %	40 %
Elongation at Yield	12 %	12 %
Tensile Modulus	2.60 GPa	377 ksi
Charpy Impact Unnotched	5.00 J/cmÂ²	23.8 ft-lb/inÂ²
Charpy Impact, Notched	0.520 J/cmÂ²	2.47 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.13	0.13
Coefficient of Friction, Static	0.15	0.15
K (wear) Factor	1.80 x 10^-8 mmÂ³/N-M	0.894 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	150 Â°C	302 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	100 Â°C	212 Â°F
Vicat Softening Point	130 Â°C @Load 5.00 kg	266 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	175 - 200 Â°C	347 - 392 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa