LATI Latilub 66-20T G/20 PA66, 20% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 66-20T G/20 PA66, 20% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0095 - 0.0125 cm/cm
0.0095 - 0.0125 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 6.30 GPa
914 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Coefficient of Friction, Dynamic 0.22
0.22
Coefficient of Friction, Static 0.30
0.30
K (wear) Factor 5.50 x 10-8 mm³/N-M
2.73 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 265 °C
509 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 250 °C

@Load 5.00 kg
482 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa