LATI Latilub 66-01M PA66, Molybdenum disulphide Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 66-01M PA66, Molybdenum disulphide Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Linear Mold Shrinkage, Flow 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse 0.0125 - 0.0155 cm/cm
0.0125 - 0.0155 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
Elongation at Break 11 %
11 %
Elongation at Yield 9.0 %
9.0 %
Tensile Modulus 3.70 GPa
537 ksi
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Coefficient of Friction, Dynamic 0.27
0.27
Coefficient of Friction, Static 0.29
0.29
K (wear) Factor 70.0 x 10-8 mm³/N-M
34.7 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Vicat Softening Point 240 °C

@Load 5.00 kg
464 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa