LATI Latilub 62-01M G/30 PA6, 30% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 62-01M G/30 PA6, 30% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyamide 6 (PA6). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.36 g/cc	0.0491 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0040 - 0.0055 cm/cm	0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse	0.0075 - 0.010 cm/cm	0.0075 - 0.010 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	160 MPa	23200 psi
Elongation at Break	3.0 %	3.0 %
Tensile Modulus	8.80 GPa	1280 ksi
Charpy Impact Unnotched	7.00 J/cmÂ²	33.3 ft-lb/inÂ²
Charpy Impact, Notched	0.900 J/cmÂ²	4.28 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.38	0.38
Coefficient of Friction, Static	0.45	0.45
K (wear) Factor	31.0 x 10^-8 mmÂ³/N-M	15.4 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	220 Â°C	428 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	200 Â°C	392 Â°F
Vicat Softening Point	210 Â°C @Load 5.00 kg	410 Â°F @Load 11.0 lb
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English
Melt Temperature	240 - 280 Â°C	464 - 536 Â°F
Mold Temperature	70.0 - 100 Â°C	158 - 212 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa