LATI Latilub 45/7-20T HDPE, PTFE Reinforced

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 45/7-20T HDPE, PTFE Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on High density polyethylene (HD-PE). PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.06 g/cc	0.0383 lb/inÂ³
Linear Mold Shrinkage, Flow	0.011 - 0.015 cm/cm	0.011 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.011 - 0.015 cm/cm	0.011 - 0.015 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	20.0 MPa	2900 psi
Elongation at Break	20 %	20 %
Elongation at Yield	10 %	10 %
Tensile Modulus	1.40 GPa	203 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.12	0.12
Coefficient of Friction, Static	0.17	0.17
K (wear) Factor	6.00 x 10^-8 mmÂ³/N-M	2.98 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	75.0 Â°C	167 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	45.0 Â°C	113 Â°F
Vicat Softening Point	70.0 Â°C @Load 5.00 kg	158 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	180 - 230 Â°C	356 - 446 Â°F
Mold Temperature	20.0 - 40.0 Â°C	68.0 - 104 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa