LATI Latilon 28D G/20-V0 PC, 20% Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latilon
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilon 28D G/20-V0 PC, 20% Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate (PC) based compound. Glass fibers. UL94 V-0 classified, brominated and chlorinated halogens-based flame retardants free. Low smoke density and low toxicity index. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa

@Temperature 120 °C
 8700 psi

@Temperature 248 °F
70.0 MPa

@Temperature 90.0 °C
 10200 psi

@Temperature 194 °F
85.0 MPa

@Temperature 60.0 °C
 12300 psi

@Temperature 140 °F
95.0 MPa

@Temperature 23.0 °C
 13800 psi

@Temperature 73.4 °F
Elongation at Break 1.5 %

@Temperature 90.0 °C
 1.5 %

@Temperature 194 °F
1.5 %

@Temperature 120 °C
 1.5 %

@Temperature 248 °F
1.6 %

@Temperature 60.0 °C
 1.6 %

@Temperature 140 °F
1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
Tensile Modulus 4.50 GPa

@Temperature 120 °C
 653 ksi

@Temperature 248 °F
5.70 GPa

@Temperature 90.0 °C
 827 ksi

@Temperature 194 °F
6.00 GPa

@Temperature 60.0 °C
 870 ksi

@Temperature 140 °F
6.50 GPa

@Temperature 23.0 °C
 943 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
 284 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Comparative Tracking Index 150 V
150 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 100 - 120 °C
212 - 248 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa