LATI Latigray 53/22-01 CX/25 PP Homopolymer, Impact Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer LATI
Trade Name Latigray
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latigray 53/22-01 CX/25 PP Homopolymer, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
Linear Mold Shrinkage, Flow 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
Linear Mold Shrinkage, Transverse 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 18.0 MPa

@Temperature 23.0 °C
 2610 psi

@Temperature 73.4 °F
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
Elongation at Yield 6.0 %

@Temperature 23.0 °C
 6.0 %

@Temperature 73.4 °F
8.5 %

@Temperature 60.0 °C
 8.5 %

@Temperature 140 °F
9.0 %

@Temperature 90.0 °C
 9.0 %

@Temperature 194 °F
Tensile Modulus 0.650 GPa

@Temperature 90.0 °C
 94.3 ksi

@Temperature 194 °F
1.10 GPa

@Temperature 60.0 °C
 160 ksi

@Temperature 140 °F
2.60 GPa

@Temperature 23.0 °C
 377 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
 7.14 ft-lb/in²

@Temperature -4.00 °F
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.100 J/cm²

@Temperature -20.0 °C
 0.476 ft-lb/in²

@Temperature -4.00 °F
0.350 J/cm²

@Temperature 23.0 °C
 1.67 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 24 %
24 %
Glow Wire Test 750 °C

@Thickness 1.00 mm
 1380 °F

@Thickness 0.0394 in
 GWFI/GWT
750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 200 - 240 °C
392 - 464 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa