LATI Laticonther 92 GR/65 PUR, 65% Graphite Reinforced

Category	Polymer , Thermoplastic , Polyurethane, TP
Manufacturer	LATI
Trade Name	Laticonther
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Laticonther 92 GR/65 PUR, 65% Graphite Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High thermal conductivity product based on Polyurethane (PUR). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.72 g/cc	0.0621 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0030 - 0.0045 cm/cm	0.0030 - 0.0045 in/in
Linear Mold Shrinkage, Transverse	0.0030 - 0.0045 cm/cm	0.0030 - 0.0045 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	20.0 MPa	2900 psi
Elongation at Break	8.0 %	8.0 %
Tensile Modulus	1.10 GPa	160 ksi
Charpy Impact Unnotched	1.50 J/cmÂ²	7.14 ft-lb/inÂ²
Charpy Impact, Notched	0.750 J/cmÂ²	3.57 ft-lb/inÂ²

Thermal Properties	Metric	English	Comments
Thermal Conductivity	10.0 W/m-K	69.4 BTU-in/hr-ftÂ²-Â°F	Longitudinal
Deflection Temperature at 0.46 MPa (66 psi)	100 Â°C	212 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	65.0 Â°C	149 Â°F
Vicat Softening Point	85.0 Â°C @Load 5.00 kg	185 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	190 - 230 Â°C	374 - 446 Â°F
Mold Temperature	20.0 - 40.0 Â°C	68.0 - 104 Â°F
Drying Temperature	70.0 - 90.0 Â°C @Time 10800 sec	158 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa