LATI Laticonther 62 CPG/750 PA 6, Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	LATI
Trade Name	Laticonther
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Laticonther 62 CPG/750 PA 6, Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High thermal conductivity product based on Polyamide 6 (PA6). Special filler. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	2.56 g/cc	0.0925 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0035 - 0.0055 cm/cm	0.0035 - 0.0055 in/in
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	80.0 MPa	11600 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	11.4 GPa	1650 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²

Thermal Properties	Metric	English	Comments
Thermal Conductivity	1.70 W/m-K	11.8 BTU-in/hr-ftÂ²-Â°F	Longitudinal
Maximum Service Temperature, Air	90.0 Â°C	194 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	215 Â°C	419 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	190 Â°C	374 Â°F
Vicat Softening Point	195 Â°C @Load 5.00 kg	383 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm

Processing Properties	Metric	English
Melt Temperature	250 - 290 Â°C	482 - 554 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa