LATI Latiblend 7587 E61-V0 PBT/PC, Flame Retardant

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	LATI
Trade Name	Latiblend
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiblend 7587 E61-V0 PBT/PC, Flame Retardant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blend based on Polybutylene Terephthalate (PBT) / Polycarbonate (PC). Toughened. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Very high dimensional stability. High impact resistance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.33 g/cc	0.0480 lb/in³
Linear Mold Shrinkage, Flow	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	20.0 MPa @Temperature 60.0 °C	2900 psi @Temperature 140 °F
	30.0 MPa @Temperature 23.0 °C	4350 psi @Temperature 73.4 °F
Elongation at Break	20 % @Temperature 23.0 °C	20 % @Temperature 73.4 °F
	75 % @Temperature 60.0 °C	75 % @Temperature 140 °F
	>= 100 % @Temperature 90.0 °C	>= 100 % @Temperature 194 °F
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F
Elongation at Yield	5.0 % @Temperature 23.0 °C	5.0 % @Temperature 73.4 °F
	>= 10 % @Temperature 60.0 °C	>= 10 % @Temperature 140 °F
	>= 10 % @Temperature 90.0 °C	>= 10 % @Temperature 194 °F
	>= 10 % @Temperature 120 °C	>= 10 % @Temperature 248 °F
Tensile Modulus	1.00 GPa @Temperature 120 °C	145 ksi @Temperature 248 °F
	1.20 GPa @Temperature 90.0 °C	174 ksi @Temperature 194 °F
	1.40 GPa @Temperature 60.0 °C	203 ksi @Temperature 140 °F
	1.90 GPa @Temperature 23.0 °C	276 ksi @Temperature 73.4 °F
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	2.00 J/cm²	9.52 ft-lb/in²

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	130 °C	266 °F
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F
Deflection Temperature at 1.8 MPa (264 psi)	75.0 °C	167 °F
Vicat Softening Point	120 °C @Load 5.00 kg	248 °F @Load 11.0 lb
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in
	V-0 @Thickness 15.0 mm	V-0 @Thickness 0.591 in
Oxygen Index	29 %	29 %
Glow Wire Test	960 °C @Thickness 1.00 mm	1760 °F @Thickness 0.0394 in	GWFI/GWT
	960 °C @Thickness 2.00 mm	1760 °F @Thickness 0.0787 in	GWFI/GWT

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	200 V	200 V	A solution

Processing Properties	Metric	English
Melt Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	120 - 130 °C @Time 10800 sec	248 - 266 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa