LATI Later 4E61 GCER/450-V0 PBT, Glass/Mineral Filled, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass + Mineral Filled
Manufacturer LATI
Trade Name Later
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4E61 GCER/450-V0 PBT, Glass/Mineral Filled, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Toughened. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Very good electrical properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 150 °C
4350 psi

@Temperature 302 °F
40.0 MPa

@Temperature 120 °C
5800 psi

@Temperature 248 °F
50.0 MPa

@Temperature 90.0 °C
7250 psi

@Temperature 194 °F
65.0 MPa

@Temperature 60.0 °C
9430 psi

@Temperature 140 °F
95.0 MPa

@Temperature 23.0 °C
13800 psi

@Temperature 73.4 °F
Elongation at Break 1.7 %

@Temperature 23.0 °C
1.7 %

@Temperature 73.4 °F
2.0 %

@Temperature 60.0 °C
2.0 %

@Temperature 140 °F
2.4 %

@Temperature 90.0 °C
2.4 %

@Temperature 194 °F
2.8 %

@Temperature 120 °C
2.8 %

@Temperature 248 °F
3.0 %

@Temperature 150 °C
3.0 %

@Temperature 302 °F
Tensile Modulus 2.70 GPa

@Temperature 150 °C
392 ksi

@Temperature 302 °F
3.50 GPa

@Temperature 120 °C
508 ksi

@Temperature 248 °F
5.00 GPa

@Temperature 90.0 °C
725 ksi

@Temperature 194 °F
7.80 GPa

@Temperature 60.0 °C
1130 ksi

@Temperature 140 °F
11.0 GPa

@Temperature 23.0 °C
1600 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
401 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Oxygen Index 30 %
30 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
GWFI/GWT
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 475 V
475 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 255 °C
464 - 491 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa