LATI Latamid 68 H2-V0 PA6/PA66 copolymer, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 68 H2-V0 PA6/PA66 copolymer, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA6/PA66 copolymer (PA6/PA66) based compound. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Linear Mold Shrinkage, Flow 0.0085 - 0.011 cm/cm
0.0085 - 0.011 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 10 %

@Temperature 23.0 °C
 10 %

@Temperature 73.4 °F
60 %

@Temperature 60.0 °C
 60 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 3.0 %
3.0 %
Tensile Modulus 0.650 GPa

@Temperature 150 °C
 94.3 ksi

@Temperature 302 °F
0.850 GPa

@Temperature 120 °C
 123 ksi

@Temperature 248 °F
1.10 GPa

@Temperature 90.0 °C
 160 ksi

@Temperature 194 °F
2.00 GPa

@Temperature 60.0 °C
 290 ksi

@Temperature 140 °F
3.40 GPa

@Temperature 23.0 °C
 493 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
9.00 J/cm²

@Temperature -20.0 °C
 42.8 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.250 J/cm²

@Temperature -20.0 °C
 1.19 ft-lb/in²

@Temperature -4.00 °F
0.300 J/cm²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Vicat Softening Point 210 °C

@Load 5.00 kg
 410 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 30 %
30 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 245 - 260 °C
473 - 500 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa