LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 66 (PA66) based compound. Oil stabilized. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0065 cm/cm | 0.0035 - 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa @Temperature 150 °C |
12300 psi @Temperature 302 °F |
|
| 100 MPa @Temperature 120 °C |
14500 psi @Temperature 248 °F |
||
| 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
||
| 140 MPa @Temperature 60.0 °C |
20300 psi @Temperature 140 °F |
||
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
||
| Elongation at Break | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
|
| 3.2 % @Temperature 60.0 °C |
3.2 % @Temperature 140 °F |
||
| 4.2 % @Temperature 90.0 °C |
4.2 % @Temperature 194 °F |
||
| 4.6 % @Temperature 120 °C |
4.6 % @Temperature 248 °F |
||
| 4.9 % @Temperature 150 °C |
4.9 % @Temperature 302 °F |
||
| Tensile Modulus | 4.40 GPa @Temperature 150 °C |
638 ksi @Temperature 302 °F |
|
| 5.80 GPa @Temperature 120 °C |
841 ksi @Temperature 248 °F |
||
| 7.90 GPa @Temperature 90.0 °C |
1150 ksi @Temperature 194 °F |
||
| 9.20 GPa @Temperature 60.0 °C |
1330 ksi @Temperature 140 °F |
||
| 10.2 GPa @Temperature 23.0 °C |
1480 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Vicat Softening Point | 255 °C @Load 5.00 kg |
491 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Polymer Resources PC-G40 Polycarbonate, 40% Glass Reinforced
- PolyOne Geon™ Vinyl Flexible R5230C Polyvinyl Chloride, Flexible (PVC, Flexible)
- Abatron AboCast 8-14/Abocure 8-14 Epoxy (discontinued **)
- Fine Organics FINALUX GH 5 Lubricant Additive
- Gwent Electronic Materials C2050303D1 Fine Line Printing Ink
- LATI Latistat 66-06 G/30 PA66, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific)
- A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene
- Barlog Plastics KEBAFLEX U A 75 ST B01 natural TPU, Shore A75, natural
Copyright © lookpolymers.com All Rights Reserved