LATI Latamid 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0085 cm/cm
0.0055 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Temperature 150 °C
 14500 psi

@Temperature 302 °F
120 MPa

@Temperature 120 °C
 17400 psi

@Temperature 248 °F
135 MPa

@Temperature 90.0 °C
 19600 psi

@Temperature 194 °F
160 MPa

@Temperature 60.0 °C
 23200 psi

@Temperature 140 °F
220 MPa

@Temperature 23.0 °C
 31900 psi

@Temperature 73.4 °F
Elongation at Break 1.7 %

@Temperature 23.0 °C
 1.7 %

@Temperature 73.4 °F
2.3 %

@Temperature 60.0 °C
 2.3 %

@Temperature 140 °F
3.0 %

@Temperature 90.0 °C
 3.0 %

@Temperature 194 °F
3.2 %

@Temperature 120 °C
 3.2 %

@Temperature 248 °F
3.4 %

@Temperature 150 °C
 3.4 %

@Temperature 302 °F
Tensile Modulus 7.70 GPa

@Temperature 150 °C
 1120 ksi

@Temperature 302 °F
10.5 GPa

@Temperature 120 °C
 1520 ksi

@Temperature 248 °F
15.0 GPa

@Temperature 90.0 °C
 2180 ksi

@Temperature 194 °F
21.5 GPa

@Temperature 60.0 °C
 3120 ksi

@Temperature 140 °F
22.5 GPa

@Temperature 23.0 °C
 3260 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 5000 ohm-cm
5000 ohm-cm
Surface Resistance 1000 ohm
1000 ohm
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: