LATI Latamid 66 H2 K/20 PA 66, 20% Carbon Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 K/20 PA 66, 20% Carbon Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0095 cm/cm
0.0065 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa

@Temperature 150 °C
13100 psi

@Temperature 302 °F
105 MPa

@Temperature 120 °C
15200 psi

@Temperature 248 °F
115 MPa

@Temperature 90.0 °C
16700 psi

@Temperature 194 °F
140 MPa

@Temperature 60.0 °C
20300 psi

@Temperature 140 °F
200 MPa

@Temperature 23.0 °C
29000 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
2.0 %

@Temperature 73.4 °F
2.7 %

@Temperature 60.0 °C
2.7 %

@Temperature 140 °F
3.4 %

@Temperature 90.0 °C
3.4 %

@Temperature 194 °F
3.6 %

@Temperature 120 °C
3.6 %

@Temperature 248 °F
3.7 %

@Temperature 150 °C
3.7 %

@Temperature 302 °F
Tensile Modulus 5.40 GPa

@Temperature 150 °C
783 ksi

@Temperature 302 °F
7.50 GPa

@Temperature 120 °C
1090 ksi

@Temperature 248 °F
10.0 GPa

@Temperature 90.0 °C
1450 ksi

@Temperature 194 °F
14.0 GPa

@Temperature 60.0 °C
2030 ksi

@Temperature 140 °F
15.5 GPa

@Temperature 23.0 °C
2250 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 250 °C

@Load 5.00 kg
482 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 50000 ohm-cm
50000 ohm-cm
Surface Resistance 5000 ohm
5000 ohm
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Copyright © lookpolymers.com All Rights Reserved