LATI Latamid 66 H2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa

@Temperature 150 °C
 13100 psi

@Temperature 302 °F
105 MPa

@Temperature 120 °C
 15200 psi

@Temperature 248 °F
115 MPa

@Temperature 90.0 °C
 16700 psi

@Temperature 194 °F
145 MPa

@Temperature 60.0 °C
 21000 psi

@Temperature 140 °F
185 MPa

@Temperature 23.0 °C
 26800 psi

@Temperature 73.4 °F
Elongation at Break 2.8 %

@Temperature 23.0 °C
 2.8 %

@Temperature 73.4 °F
3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
4.7 %

@Temperature 90.0 °C
 4.7 %

@Temperature 194 °F
5.2 %

@Temperature 120 °C
 5.2 %

@Temperature 248 °F
5.6 %

@Temperature 150 °C
 5.6 %

@Temperature 302 °F
Tensile Modulus 4.90 GPa

@Temperature 150 °C
 711 ksi

@Temperature 302 °F
6.20 GPa

@Temperature 120 °C
 899 ksi

@Temperature 248 °F
8.30 GPa

@Temperature 90.0 °C
 1200 ksi

@Temperature 194 °F
9.50 GPa

@Temperature 60.0 °C
 1380 ksi

@Temperature 140 °F
10.5 GPa

@Temperature 23.0 °C
 1520 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: