LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 E21 G/15 PA 66, 15% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Toughened. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.013 cm/cm
0.010 - 0.013 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 150 °C
 4350 psi

@Temperature 302 °F
35.0 MPa

@Temperature 120 °C
 5080 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
65.0 MPa

@Temperature 60.0 °C
 9430 psi

@Temperature 140 °F
90.0 MPa

@Temperature 23.0 °C
 13100 psi

@Temperature 73.4 °F
Elongation at Break 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
7.5 %

@Temperature 60.0 °C
 7.5 %

@Temperature 140 °F
8.6 %

@Temperature 90.0 °C
 8.6 %

@Temperature 194 °F
9.3 %

@Temperature 120 °C
 9.3 %

@Temperature 248 °F
9.5 %

@Temperature 150 °C
 9.5 %

@Temperature 302 °F
Elongation at Yield 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
4.8 %

@Temperature 60.0 °C
 4.8 %

@Temperature 140 °F
6.1 %

@Temperature 90.0 °C
 6.1 %

@Temperature 194 °F
6.6 %

@Temperature 120 °C
 6.6 %

@Temperature 248 °F
6.9 %

@Temperature 150 °C
 6.9 %

@Temperature 302 °F
Tensile Modulus 1.70 GPa

@Temperature 150 °C
 247 ksi

@Temperature 302 °F
1.90 GPa

@Temperature 120 °C
 276 ksi

@Temperature 248 °F
2.50 GPa

@Temperature 90.0 °C
 363 ksi

@Temperature 194 °F
3.40 GPa

@Temperature 60.0 °C
 493 ksi

@Temperature 140 °F
4.80 GPa

@Temperature 23.0 °C
 696 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
8.00 J/cm²

@Temperature -20.0 °C
 38.1 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 1.50 J/cm²

@Temperature -20.0 °C
 7.14 ft-lb/in²

@Temperature -4.00 °F
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Vicat Softening Point 230 °C

@Load 5.00 kg
 446 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa