LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/30-V0HF1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good electrical properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0090 cm/cm
0.0065 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 150 °C
9430 psi

@Temperature 302 °F
75.0 MPa

@Temperature 120 °C
10900 psi

@Temperature 248 °F
80.0 MPa

@Temperature 90.0 °C
11600 psi

@Temperature 194 °F
105 MPa

@Temperature 60.0 °C
15200 psi

@Temperature 140 °F
145 MPa

@Temperature 23.0 °C
21000 psi

@Temperature 73.4 °F
Elongation at Break 3.2 %

@Temperature 23.0 °C
3.2 %

@Temperature 73.4 °F
4.6 %

@Temperature 60.0 °C
4.6 %

@Temperature 140 °F
6.7 %

@Temperature 90.0 °C
6.7 %

@Temperature 194 °F
7.6 %

@Temperature 120 °C
7.6 %

@Temperature 248 °F
8.6 %

@Temperature 150 °C
8.6 %

@Temperature 302 °F
Tensile Modulus 3.40 GPa

@Temperature 150 °C
493 ksi

@Temperature 302 °F
3.80 GPa

@Temperature 120 °C
551 ksi

@Temperature 248 °F
4.60 GPa

@Temperature 90.0 °C
667 ksi

@Temperature 194 °F
7.50 GPa

@Temperature 60.0 °C
1090 ksi

@Temperature 140 °F
10.5 GPa

@Temperature 23.0 °C
1520 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
419 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Oxygen Index 32 %
32 %
Glow Wire Test 755 °C

@Thickness 2.00 mm
1390 °F

@Thickness 0.0787 in
GWIT
775 °C

@Thickness 1.00 mm
1430 °F

@Thickness 0.0394 in
GWIT
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
GWFI/GWT
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa